A criterion of the metastable extension of solid solubility was proposed.When the eutectic concentration arm ratio parameter of an alloy,J>10,the hypereutectic extension and the metastable solid solubility limit beyond eutectic concentration may be obtained.When J≤10, the hypoeutectic extension may be obtained.The extension parameter,C_(eq)~s/C_(cu),is directly proportional to the parameter J.Thus,it seems easy to predict the tendency of the solid solu- hility extension under rapid solidification on the basis of the eutectic phase diagram.
关键词:
eutectic system
,
null
,
null
廖春发
,
房孟钊
,
王旭
,
杨少华
,
罗林生
稀有金属
doi:10.13373/j.cnki.cjrm.2016.08.007
采用铂丝(RE)-钨丝(WE)-钨棒(AE)组成三电极系统,通过计时电流法与计时电位法相结合,系统分析在一定温度及配比条件下NaCl-KCl-Na2WO4共融体系的电化学特性,重点考察和分析钨(Ⅵ)离子的电子转移步骤、电化学还原过程的可逆性、活性钨(Ⅵ)离子的扩散系数、钨金属单质的成核过程,结果表明:计时电流曲线得出钨(Ⅵ)离子在阴极区的电极过程是由扩散控制,扩散系数为1.645×10-10cm2·s-1,金属钨在阴极上析出为三维瞬时形核过程,不存在成核极化现象;由计时电位法得出钨(Ⅵ)离子的电极还原过程亦为扩散控制,扩散系数为2.349 ×10-11 cm2·s-1,钨(Ⅵ)离子在电子转移过程分两步,第一步为钨(Ⅵ)离子→钨(Ⅳ)离子的2电子转移,其为准可逆反应,第二步为钨(Ⅳ)离子→钨(0)的4电子转移过程,此过程为高度不可逆反应.同时,采用不同的电化学方法得到的活性钨(Ⅵ)离子的扩散系数差异表明实验过程中存在时效性和偶然性因素影响,对扩散系数等动力学参数的计算有待优化.
关键词:
共融体系
,
电化学特性
,
电极过程
,
计时电流法
,
计时电位法